3M™ Dyneon™ Products > Fluoroelastomers >

Fluoroelastomer Copolymers

Dyneon Fluoroelastomer Copolymers have excellent resistance to heat & chemicals and also provide outstanding processability and permeation resistance. The preferred choice of processors and end users -Dyneon's full line of fluoroelastomers (FKMs) provide flexibility in choosing the right material for critical sealing applications.

Dyneon™ Fluoroelastomer Copolymers contain 65.9% Fluorine

Find out Where to Buy our Products.

Product Name	Typical Properties*	MSDS	Data Sheets
Dyneon™ FC 2110Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 19 Cure Technology: Incorporated Cure Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 13.8 MPa (2,010 psi)
Dyneon™ FC 2120	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 16 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 23 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 14.7 MPa (2,140 psi)
Dyneon™ FC 2121	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 14 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 24 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.4 MPa (2,375 psi)
Dyneon™ FC 2122	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 25 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 25 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 13.1 MPa (1,900 psi)
Dyneon™ FC 2123	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 20 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 25 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.2 MPa (2,350 psi)
Dyneon™ FC 2144	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 17 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 41 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 17.5 MPa (2,540 psi)
Dyneon™ FC 2145	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 16 Cure Technology: Raw Gum Mooney Viscosity - ML1 + 10 @ 121 °C: 28 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 12.2 MPa (1,765 psi)
Dyneon™ FC 2152	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 22 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 51 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 14.5 MPa (2,100 psi)
Dyneon™ FC 2170	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 18 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 31 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 13.8 MPa (2,000 psi)
Dyneon™ FC 2174	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 12 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 40 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.9 MPa (2,450 psi)
Dyneon™ FC 2176	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 22 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 30 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 15 MPa (2,175 psi)
Dyneon™ FC 2177D	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 21 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 33 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 12.8 MPa (1,865 psi)
Dyneon™ FC 2178	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 10 Cure Technology: Raw Gum Mooney Viscosity - ML1 + 10 @ 121 °C: 100 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 15.7 MPa (2,275 psi)
Dyneon™ FC 2179	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 10 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 80 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 17.1 MPa (2,475 psi)
Dyneon™ FC 2180	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 12 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 40 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.3 MPa (2,370 psi)
Dyneon™ FC 2181	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 44 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 17.6 MPa (2,560 psi)
Dyneon™ FC 2182	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 22 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 30 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 13.5 MPa (1,960 psi)
Dyneon™ FC 2210X	Cure Technology: Raw Gum Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C
Dyneon™ FC 2211	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 17 Cure Technology: Raw Gum Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 12.9 MPa (1,870 psi)
Dyneon™ FC 2230	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 15 Cure Technology: Raw Gum Mooney Viscosity - ML1 + 10 @ 121 °C: 38 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 13.7 MPa (1,995 psi)
Dyneon™ FC 2260	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 25 Cure Technology: Raw Gum Mooney Viscosity - ML1 + 10 @ 121 °C: 60 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.2 MPa (2,345 psi)
Dyneon™ FC 2261Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 14 Cure Technology: Raw Gum Mooney Viscosity - ML1 + 10 @ 121 °C: 63 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C 12.9 MPa (1,870 psi)
Dyneon™ FE 5520X	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 20 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 26 Post Cure: 24 h @ 260°C Press Cure: 5 min @ 170°C Tensile MPa (psi) 13.8 MPa (2,000 psi)
Dyneon™ FE 5542X	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 18 Cure Technology: Raw Gum Mooney Viscosity - ML1 + 10 @ 121 °C: 42 Post Cure: 24 h @ 260°C Press Cure: 5 min @ 170°C Tensile MPa (psi) 14.5 MPa (2,100 psi)
Dyneon™ FE 5610	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 21 Cure Technology: Incorporated Cure Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 13.3 MPa (1,930 psi)
Dyneon™ FE 5620Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 23 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 15.4 MPa (2,240 psi)
Dyneon™ FE 5621	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 23 Post Cure: 24 h @ 260°C Press Cure: 5 min @ 177°C Tensile MPa (psi) 15.4 MPa (2,240 psi)
Dyneon™ FE 5622Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 18 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 22 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.2 MPa (2,350 psi)
Dyneon™ FE 5623	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 24 Post Cure: 24 h @ 250°C Press Cure: 5 min @ 177°C Tensile MPa (psi) 15.8 MPa (2,300 psi)
Dyneon™ FE 5640Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 11 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 40 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.3 MPa (2,370 psi)
Dyneon™ FE 5641Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 11 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 40 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.1 MPa (2,340 psi)
Dyneon™ FE 5642	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 17 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 42 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 17.4 MPa (2,530 psi)
Dyneon™ FE 5643Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 11 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 40 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.5 MPa (2,400 psi)
Dyneon™ FE 5660Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 9 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 60 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.5 MPa (2,400 psi)
Dyneon™ FG 5630Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 30 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 14.7 MPa (2,140 psi)
Dyneon™ FG 5661X	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 14 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 60 Post Cure: 24 h @ 260°C Press Cure: 5 min @ 177°C Tensile MPa (psi) 15.3 MPa (2,223 psi)
Dyneon™ FG 5690Q	Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 10 Cure Technology: Incorporated Cure Mooney Viscosity - ML1 + 10 @ 121 °C: 97 Post Cure: 24 h @ 250°C Press Cure: 7 min @ 177°C Tensile MPa (psi) 16.3 MPa (2,360 psi)

Product Features

Some of the features of Dyneon Fluroelastometers include:

Broad Chemical Resistance

Temperature resistance - 18 to 250°C

Low permeation

Typical Applications

Dyneon Fluroelastometers are used in O-rings, seals, gaskets and hoses for the following markets:

Automotive Powertrain

Transportation Fuel Systems

Lubricant Application

Chemical Processing

Oil and Gas Exploration

Brochure

Dyneon™ Fluoropolymers for toughest jobs in Chemical Processing - Brochure (PDF 773.5 K)
High-performance Dyneon™ Fluoroelastomers - Brochure (PDF 2.2 MB)

Regulatory Material

Dyneon™ Fluoropolymers

Industry Solutions

Product Information

Resources

Customer Support

Fluoroelastomer Copolymers