3M™ Dyneon™ Products > Fluoroelastomers > 

Fluoroelastomer Terpolymers


Fluoroelastomer Terpolymers
Click to Enlarge

Dyneon Fluoroelastomer Terpolymers have excellent resistance to heat & chemicals and also provide outstanding processability and permeation resistance. The preferred choice of processors and end users -Dyneon's full line of fluoroelastomers (FKMs) provide flexibility in choosing the right material for critical sealing applications.

Dyneon™ Fluoroelastomer Terpolymers contain 65.5% to 70% Fluorine
Find out Where to Buy our Products.

Product Name Typical Properties* MSDS Data Sheets
Dyneon™ FE 5522X  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 20
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 29
Post Cure: 24 h @ 260°C
Press Cure: 5 min @ 177°C
Tensile MPa (psi) 13.8 MPa (2,010 psi)

 PDF   PDF  
Dyneon™ FE 5730  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 45
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 36
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 10.5 MPa (1,460 psi)

   PDF  
Dyneon™ FE 5830Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 44
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 33
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 11 MPa (1,600 psi)

 PDF   PDF  
Dyneon™ FE 5840Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 26
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 37
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.8 MPa (2,010 psi)

 PDF   PDF  
Dyneon™ FLS 2530  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 19
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 39
Post Cure: 24 h @ 230°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 15.2 MPa (2,200 psi)

 PDF   PDF  
Dyneon™ FLS 2650  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 28
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 50
Post Cure: 24 h @ 230°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 18.0 MPa (2,600 psi)

 PDF   PDF  
Dyneon™ FPO 3740  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 36
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 38
Post Cure: 2h @ 180°C
Press Cure: 15 min @ 180°C
Tensile MPa (psi) 17.8 MPa (2,580 psi)

 PDF   PDF  
Dyneon™ FPO 3741  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 30
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 38
Post Cure: 2h @ 180°C
Press Cure: 15 min @ 180°C
Tensile MPa (psi) 18.0 MPa (2,610 psi)

 PDF   PDF  
Dyneon™ FT 2320  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 39
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 23
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.8 MPa (2,010 psi)

 PDF   PDF  
Dyneon™ FT 2350  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 36
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 56
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 15.2 MPa (2,210 psi)

 PDF    
Dyneon™ FT 2430  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 38
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 31
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.4 MPa (1,950 psi)

 PDF    
Dyneon™ FT 2481  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 24
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 75
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 15.2 MPa (2,200 psi)

 PDF    
Product Features
Some of the features of Dyneon Fluroelastometers include:

  • Broad Chemical Resistance
  • Temperature resistance - 18 to 250°C
  • Low permeation

    		•
    Typical Applications
    Dyneon Fluroelastometers are used in O-rings, seals, gaskets and hoses for the following markets:

  • Automotive Powertrain
  • Transportation Fuel Systems
  • Lubricant Application
  • Chemical Processing
  • Oil and Gas Exploration