PFA Fluoroplastics


PFA Fluoroplastics
Click to Enlarge

Dyneon™ PFA (a polymer of tetrafluoroethylene and perfluorovinylether) has exceptional heat resistance, excellent electrical properties and excellent chemical and weather resistance. It is also used in several chemical industry and home appliance coatings applications.

This product line was recently expanded to include ultra high purity (UHP) grades for applications requiring low metal and anion extractables and low outgassing.
Find out Where to Buy our Products.

Product Name Typical Properties* MSDS Data Sheets
Dyneon™ PFA 6502N Z Fluorothermoplastic -3MID- 97500013657 113736446 

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 550 MPa (80,000 psi)
Melt Flow Index (MFI): 2 g/10 min.
Melting Point °C (°F) - ASTM 4591: 310°C (590°F)

 PDF   PDF  
Dyneon™ PFA 6515 UHP  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 620 MPa (90,000 psi)
Melt Flow Index (MFI): 15 g/10 min.
Melting Point °C (°F) - ASTM 4591: 310°C (590°F)

 PDF    
Dyneon™ PFA 6515N  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 620 MPa (90,000 psi)
Melt Flow Index (MFI): 15 g/10 min.
Melting Point °C (°F) - ASTM 4591: 310°C (590°F)

 PDF   PDF  
Dyneon™ PFA 6515T  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 620 MPa (90,000 psi)
Melt Flow Index (MFI): 15 g/10 min.
Melting Point °C (°F) - ASTM 4591: 310°C (590°F)

 PDF    
Dyneon™ PFA-FLEX 8502 UHP  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 600 MPa (87,000 psi)
Melt Flow Index (MFI): 2 g/10 min.
Melting Point °C (°F) - ASTM 4591: 290°C (554°F)

 PDF    
Dyneon™ PFA-FLEX 8515 UHP  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 600 MPa (87,000 psi)
Melt Flow Index (MFI): 15 g/10 min.
Melting Point °C (°F) - ASTM 4591: 290°C (554°F)

 PDF   PDF  
E20241 DYNEON PFA 50KG/110 LB DRUM 

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 550 MPa (80,000 psi)
Melt Flow Index (MFI): 2 g/10 min.
Melting Point °C (°F) - ASTM 4591: 310°C (590°F)

   PDF  
PFA 6502T Z DYNEON PFA 50KG/110LB BOX 

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 550 MPa (80,000 psi)
Melt Flow Index (MFI): 2 g/10 min.
Melting Point °C (°F) - ASTM 4591: 310°C (590°F)

 PDF   PDF  
PFA6505T Z DYNEON PFA 50KG/110 LB BOX 

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790: 550 MPa (80,000 psi)
Melt Flow Index (MFI): 5 g/10 min.
Melting Point °C (°F) - ASTM 4591: 310°C (590°F)

 PDF    

Regulatory Material