PVDF Homopolymers


PVDF Homopolymers
Click to Enlarge

PVDF Homopolymers are ideal for a variety of applications such as pumps, valves, sheet products, pipes, tubes and fittings needing excellent chemical resistance and operating temperatures up to 150°C (302°F). Various grades are available that can be processed by injection molding, compression molding, blow molding and extrusion.
Find out Where to Buy our Products.

Product Name Typical Properties* Data Sheets
Dyneon™ PVDF 1008/0001  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 2,200 MPa (319,000 psi)
Limiting Oxygen Index - % - ASTM D 2863: 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 24 g/

 PDF  
Dyneon™ PVDF 1010/0001  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 2,100 MPa (305,000 psi)
Limiting Oxygen Index - % - ASTM D 2863: 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 6 g/1

 PDF  
Dyneon™ PVDF 1012/0001  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 2,100 MPa (305,000 psi)
Limiting Oxygen Index - % - ASTM D 2863: 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 1.5 g

  
Dyneon™ PVDF 1012/0180  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 1,420 MPa (206,000 psi)
Melting Point °C (°F) - ASTM 4591: 173°C (343°F)
Tensile Strength at Break - MPa (psi) - 23°C, 50mm/min - ASTM D 638: 33 MPa (4,800 psi)

 PDF  
Dyneon™ PVDF 6008/0001  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 2,500 MPa (362,500 psi)
Limiting Oxygen Index - % - ASTM D 2863: 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 24 g/

 PDF  
Dyneon™ PVDF 6010/0000  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 2,100 MPa (305,000 psi)
Limiting Oxygen Index - % - ASTM D 2863: 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 6 g/1

 PDF  
Dyneon™ PVDF 6010/0003  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 2,100 MPa (305,000 psi)
Limiting Oxygen Index - % - ASTM D 2863: 65
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 6 g/1

  
Dyneon™ PVDF 6012/0000  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 2,100 MPa (305,000 psi)
Limiting Oxygen Index - % - ASTM D 2863: 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 6 g/10

  
Dyneon™ PVDF 6108/0001  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 1,930 MPa (280,000 psi)
Limiting Oxygen Index - % - ASTM D 2863: 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 24 g/

 PDF  