Fluoroelastomer Copolymers


Fluoroelastomer Copolymers
Click to Enlarge

Dyneon Fluoroelastomer Copolymers have excellent resistance to heat & chemicals and also provide outstanding processability and permeation resistance. The preferred choice of processors and end users -Dyneon's full line of fluoroelastomers (FKMs) provide flexibility in choosing the right material for critical sealing applications.

Dyneon™ Fluoroelastomer Copolymers contain 65.9% Fluorine

Find out Where to Buy our Products.

Product NameTypical Properties*MSDSData Sheets
Dyneon™ FC 2110Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 19
Cure Technology: Incorporated Cure
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.8 MPa (2,010 psi)

PDF  PDF  
Dyneon™ FC 2120  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 16
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 23
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 14.7 MPa (2,140 psi)

PDF  PDF  
Dyneon™ FC 2121  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 14
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 24
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.4 MPa (2,375 psi)

PDF  PDF  
Dyneon™ FC 2122  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 25
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 25
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.1 MPa (1,900 psi)

PDF  PDF  
Dyneon™ FC 2123  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 20
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 25
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.2 MPa (2,350 psi)

PDF  PDF  
Dyneon™ FC 2144  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 17
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 41
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 17.5 MPa (2,540 psi)

PDF  PDF  
Dyneon™ FC 2145  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 16
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 28
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 12.2 MPa (1,765 psi)

PDF  PDF  
Dyneon™ FC 2152  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 22
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 51
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 14.5 MPa (2,100 psi)

PDF  PDF  
Dyneon™ FC 2170  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 18
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 31
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.8 MPa (2,000 psi)

PDF  PDF  
Dyneon™ FC 2174  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 12
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 40
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.9 MPa (2,450 psi)

PDF  PDF  
Dyneon™ FC 2176  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 22
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 30
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 15 MPa (2,175 psi)

PDF  PDF  
Dyneon™ FC 2177D  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 21
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 33
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 12.8 MPa (1,865 psi)

PDF  PDF  
Dyneon™ FC 2178  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 10
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 100
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 15.7 MPa (2,275 psi)

PDF  PDF  
Dyneon™ FC 2179  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 10
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 80
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 17.1 MPa (2,475 psi)

PDF  PDF  
Dyneon™ FC 2180  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 12
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 40
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.3 MPa (2,370 psi)

PDF  PDF  
Dyneon™ FC 2181  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 44
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 17.6 MPa (2,560 psi)

PDF  PDF  
Dyneon™ FC 2182  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 22
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 30
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.5 MPa (1,960 psi)

PDF  PDF  
Dyneon™ FC 2210X  

Cure Technology: Raw Gum
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C

PDF  PDF  
Dyneon™ FC 2211  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 17
Cure Technology: Raw Gum
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 12.9 MPa (1,870 psi)

PDF  PDF  
Dyneon™ FC 2230  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 15
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 38
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.7 MPa (1,995 psi)

PDF  PDF  
Dyneon™ FC 2260  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 25
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 60
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.2 MPa (2,345 psi)

PDF  PDF  
Dyneon™ FC 2261Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 14
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 63
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
12.9 MPa (1,870 psi)

PDF  PDF  
Dyneon™ FE 5520X  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 20
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 26
Post Cure: 24 h @ 260°C
Press Cure: 5 min @ 170°C
Tensile MPa (psi) 13.8 MPa (2,000 psi)

PDF    
Dyneon™ FE 5542X  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 18
Cure Technology: Raw Gum
Mooney Viscosity - ML1 + 10 @ 121 °C: 42
Post Cure: 24 h @ 260°C
Press Cure: 5 min @ 170°C
Tensile MPa (psi) 14.5 MPa (2,100 psi)

PDF  PDF  
Dyneon™ FE 5610  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 21
Cure Technology: Incorporated Cure
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 13.3 MPa (1,930 psi)

PDF  PDF  
Dyneon™ FE 5620Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 23
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 15.4 MPa (2,240 psi)

PDF  PDF  
Dyneon™ FE 5621  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 23
Post Cure: 24 h @ 260°C
Press Cure: 5 min @ 177°C
Tensile MPa (psi) 15.4 MPa (2,240 psi)

PDF  PDF  
Dyneon™ FE 5622Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 18
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 22
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.2 MPa (2,350 psi)

PDF  PDF  
Dyneon™ FE 5623  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 24
Post Cure: 24 h @ 250°C
Press Cure: 5 min @ 177°C
Tensile MPa (psi) 15.8 MPa (2,300 psi)

PDF  PDF  
Dyneon™ FE 5640Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 11
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 40
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.3 MPa (2,370 psi)

PDF  PDF  
Dyneon™ FE 5641Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 11
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 40
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.1 MPa (2,340 psi)

PDF  PDF  
Dyneon™ FE 5642  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 17
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 42
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 17.4 MPa (2,530 psi)

PDF  PDF  
Dyneon™ FE 5643Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 11
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 40
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.5 MPa (2,400 psi)

PDF  PDF  
Dyneon™ FE 5660Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 9
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 60
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.5 MPa (2,400 psi)

PDF  PDF  
Dyneon™ FG 5630Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 13
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 30
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 14.7 MPa (2,140 psi)

PDF  PDF  
Dyneon™ FG 5661X  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 14
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 60
Post Cure: 24 h @ 260°C
Press Cure: 5 min @ 177°C
Tensile MPa (psi) 15.3 MPa (2,223 psi)

 PDF  
Dyneon™ FG 5690Q  

Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B: 10
Cure Technology: Incorporated Cure
Mooney Viscosity - ML1 + 10 @ 121 °C: 97
Post Cure: 24 h @ 250°C
Press Cure: 7 min @ 177°C
Tensile MPa (psi) 16.3 MPa (2,360 psi)

PDF  PDF  
Product Features

Some of the features of Dyneon Fluroelastometers include:

  • Broad Chemical Resistance
  • Temperature resistance - 18 to 250°C
  • Low permeation

  • Typical Applications

    Dyneon Fluroelastometers are used in O-rings, seals, gaskets and hoses for the following markets:

  • Automotive Powertrain
  • Transportation Fuel Systems
  • Lubricant Application
  • Chemical Processing
  • Oil and Gas Exploration

    Regulatory Material