3M™ Dyneon™ Products > Fluorothermoplastics > PVDF Polymer > 

PVDF Copolymers


PVDF Copolymers
Click to Enlarge

PVDF Copolymers with HFP contain increased flexibility over PVDF homopolymer grades. Copolymers with CTFE are among the most flexible PVDF products with excellent low temperature performance and low shrinkage. Copolymers are ideal for wire & cable and tubing applications, which require enhanced flexibility.

Find out Where to Buy our Products.

Product Name Typical Properties* Data Sheets
Dyneon™ PVDF 11008/0001  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 1,000 MPa (145,000 psi)
Limiting Oxygen Index - % - ASTM D 2863 : 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 24 g

PDF  
Dyneon™ PVDF 11008/0003  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 1,000 MPa (145,000 psi)
Limiting Oxygen Index - % - ASTM D 2863 : 65
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 24 g

PDF  
Dyneon™ PVDF 11010/0000  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 900 MPa (131,000 psi)
Limiting Oxygen Index - % - ASTM D 2863 : 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 6 g/10

PDF  
Dyneon™ PVDF 31508/0001  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 425 MPa (62,000 psi)
Limiting Oxygen Index - % - ASTM D 2863 : 48
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 15 g/10

PDF  
Dyneon™ PVDF 31508/0003  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 425 MPa (62,000 psi)
Limiting Oxygen Index - % - ASTM D 2863 : 73
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 15 g/10

PDF  
Dyneon™ PVDF 31508/0009  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 425 MPa (62,000 psi)
Limiting Oxygen Index - % - ASTM D 2863 : 99.5
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 15 g/

 
Dyneon™ PVDF 32008/0009  

Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C 2mm/min - ASTM D 790 : 200 MPa (29,000 psi)
Limiting Oxygen Index - % - ASTM D 2863 : 100
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 15 g/1

PDF  
Dyneon™ PVDF 60512/0000  

Limiting Oxygen Index - % - ASTM D 2863 : 44
Melt Flow Index (MFI) - g/10 min - 230°C/5kg - ASTM D 1238: 3 g/10 min.
Melting Point °C (°F) - ASTM 4591: 173°C (343°F)

PDF  